as-cast condition
英 [æz kɑːst kənˈdɪʃn]
美 [æz kæst kənˈdɪʃn]
网络 铸造状态
双语例句
- The results show that austenite content is high and hardness is low as-cast condition.
结果表明，铸铁铸态组织含奥氏体量多，硬度低； - It is indicated that as-cast leaded brass without pretreatment can present certain superplasticity at proper condition.
结果表明：此种不经预处理的铸态铅黄铜，在适当条件下具有一定的超塑性。 - The results show that, in the as-cast condition the effect of Mo on the increasing of hardness is not as obvious as that of Cr, Cu-Cr and SPI inoculant; in the normalized condition, the effects of Mo and Cu-Cr on hardness are all outstanding.
结果发现在铸态条件，用提高硬度的作用不如铬、铜－铬以及SPI孕育剂，但在正火状态.钼的作用显著，铜－铬与之相当。 - The effect of V on nodulizing of carbides was observed in the as-cast, nomalized and oil quenched condition in low Cr white cast iron alloyed with V.
在低铬白口铸铁的基础上加入钒，观察钒含量对碳化物的团球化影响。 - Application of FZL-1 Aluminum Alloy As-cast Condition to Automobile Engine Head
FZL-1铸态铝合金性能及在汽车发动机上的应用 - The results show that with the increase of melt superheating temperature, the primary carbide MC in the as-cast condition becomes finer and more homogeneous gradually, and both the rupture life and elongation increase greatly.
结果表明：随熔体过热温度的升高，铸态组织中的初生MC碳化物不断细化和均匀分布，合金的持久断裂寿命和塑性明显提高； - Study on high chromium white cast iron containing vanadium with martensitic matrix in the as-cast condition
含钒铸态马氏体高铬铸铁的研究 - The ductile-embrittlement transition temperature of vermicular graphite cast iron increased with increasing phosphorus content both in the as-cast and annealed condition.
蠕铁的韧性&脆性转变温度铸态和退火态均随磷含量的增加而升高。 - The wear-resisting material of medium Si-Mn cast steel containing a large quantity of nodular carbide distributed in austenite matrix at as-cast condition was studied by modification method.
对中硅锰铸钢采用了变质处理方法，在铸态下获得了大量团球状碳化物分布于奥氏体基体上的抗磨材料。 - Room temperature fracture toughness was measured by three-point bending test and the KQ value for the DS condition was much higher than that for the as-cast condition. The maximum fracture toughness was 19.7MPam~ ( 1/ 2).
三点弯曲试验表明，定向凝固后试样的室温断裂韧性也得到了明显的提高，KQ最高达到了19.7MPam~（1/2）。 - Via the microstructures and mechanical properties analysis, the results indicate that the ingots of super light Mg-12wt% Li-1wt% Al as-cast alloy cast successfully in the condition of 300 ℃ mould temperature has the better casting microstructures and properties;
通过对显微组织和力学性能的分析，结果表明：超轻Mg-12%Li-Al铸造镁合金在型温为300℃浇注时，合金的铸态组织和性能比较好； - The results show that under the same wear condition, the wear resistance of Cr-Mn-Cu alloy white cast iron through water cooling and air cooling are 1.11 and 1.20 times bigger than that in as-cast condition.
结果表明，在相同的磨损条件下，水冷和空冷后的铬锰铜合金白口铸铁的耐磨性能分别是铸态的1.11倍和1.20倍；